Method for producing a capacitor

ABSTRACT

A method for producing a capacitor having a dielectric and first and second capacitor electrodes in a semiconductor circuit device formed on a semiconductor substrate, includes forming a trench in a layer applied to the substrate. An electrically conductive layer for the second capacitor electrode is deposited inside the trench and at least regionally conformally with side walls thereof. An auxiliary layer acting as a space-holder for the dielectric is conformally deposited inside the trench and on the electrically conductive layer for the second capacitor electrode. An electrically conductive layer for the first capacitor electrode is conformally deposited inside the trench and on the auxiliary layer. The auxiliary layer is at least partially removed to expose a hollow layer in at least a partial region between the two electrically conductive layers for the first and second capacitor electrodes. The dielectric is deposited into the exposed hollow layer between the two electrically conductive layers. A semiconductor memory device and a method for producing the device include producing the capacitor after production of the transistor and metallizing layers associated therewith for connection of the word and bit lines, in a configuration projecting upward from the plane; placing the capacitor in a trench formed inside a contact metallizing layer for the second electrode terminal of the transistor; and setting a depth of the trench to be equivalent to a layer thickness of the metallizing layer.

This application is a Division of Ser. No. 08/637,163 filed Apr. 24,1996 now U.S. Pat. No. 5,869,860.

BACKGROUND OF THE INVENTION FIELD OF THE INVENTION

The invention relates to a method for producing a capacitor and to asemiconductor memory device having a multiplicity of memory cellsdisposed on a semiconductor substrate, wherein each of the memory cellshas a selection transistor being disposed in a semiconductor substrateand having a gate terminal and first and second electrode terminals,each of the memory cells has a storage capacitor being associated withand triggerable by the selection transistor and having a ferroelectricdielectric and first and second capacitor electrodes, the gate terminalof each selection transistor is connected to a word line of thesemiconductor memory device, the first electrode terminal of eachselection transistor is connected to a bit line, and the first capacitorelectrode of each storage capacitor is connected to a common conductorlayer of electrically conductive material. The invention also relates toa method for producing such a semiconductor memory device.

Such a semiconductor memory device having a storage capacitor with aferroelectric dielectric (a so-called FRAM) is known, for instance, fromThe 1994 Symposium on VLSI Technology Digest of Technical Papers, pp. 55ff. by R. Moazzami et al, and from The 1994 IEEE InternationalSolid-State Circuits Conference, pp. 268 ff. by Tatsumi Sumi et al. Inthat semiconductor memory device the storage capacitors with theferroelectric dielectric are constructed in planar fashion andadditionally, because of the wiring, have cell surface areas ofconsiderable size per bit, which is considered to be disadvantageous inthe view of a desired large scale of integration. Despite the problemsthat so far still exist, a great future is predicted for ferroelectricmemories or FRAMs. They could entirely replace present semiconductormemories (DRAMs, SRAMS, EEPROMS, flash EEPROMS). The advantage of FRAMsresides above all in the brief programming time (>20 ns), a lowprogramming voltage (from about 3 V of supply voltage to the ICs), lowenergy consumption in programming (no charge pump required), andfrequent programmability (10¹² demonstrated and 101⁵ expected, ascompared with 10⁵ in EEPROMS). Examples of materials for theferroelectric layer that appear especially promising at present are leadzirconium titanate, strontium tantalate, or compounds thereof. One ofthe problems that are still an obstacle to rapid introduction of FRAMtechnology is an as-yet unsolved compatibility with a production processfor integrated circuits. In particular, the necessity for platinumelectrodes in the ferroelectric storage capacitor and spin-on coating,which heretofore has been conventional, for applying a ferroelectricgel, which is associated with a relatively great layer thickness andthus a capacitance that requires a large surface area, heretoforeprevented profitable use in semiconductor technology, so that heretoforeno process for producing FRAMs that was suitable for mass production wasknown. In that respect it must also be remembered that depositing therelatively complex materials for the ferroelectric dielectric andassociated therewith the problem of a satisfactory source suitable forthe process, and moreover a lack of quality of the layers because offissuring, leakage currents, temperature influences and electrodeadhesion, all contribute to problems of process integration. Inparticular, the ferroelectric materials known heretofore reactespecially sensitively to hydrogen. However, hydrogen can hardly besuppressed in the known methods for producing a semiconductor memorydevice, and in such methods it occurs especially in plasma depositionprocesses and plasma etching processes.

In addition to the FRAM cells, large-scale integration DRAMsemiconductor memories with conventional materials for the storagecapacitor dielectric are known. In order to make DRAM semiconductormemories with a memory capacity of up to about 256 MB at present,dielectrics with a high dielectric constant are used so that as the cellarea becomes smaller an adequate capacitance, typically of more thanabout 20 fF per cell, is still attainable. Heretofore, for thosepurposes, an ONO layer has been used in most cases, but itstechnological limits have become apparent in the meantime, since upon afurther reduction in thickness the leakage current rises above thepredetermined limit value, and adequate capacitances (surface areas) canbe obtained only through the use of such complicated structures astrench or stacked capacitors. For those reasons, new materials that havea high enough dielectric constant are therefore increasingly being usedfor the dielectric of the storage capacitor. However, the alternativedielectric materials known thus far are extremely sensitive to the usualstrains arising in the method used heretofore to produce a semiconductormemory device, namely stability to high process temperatures, undesiredchemical reactions, and the like.

SUMMARY OF THE INVENTION

It is accordingly an object of the invention to provide a method forproducing a capacitor and a semiconductor memory device, which overcomethe hereinafore-mentioned disadvantages of the heretofore-known methodsand devices of this general type, in which the semiconductor memorydevice has a ferroelectric storage capacitor that has a scale ofintegration which is virtually comparable to present DRAM circuits withsuitably high reliability and quality, and in which the method forproducing such a semiconductor memory device can be integrated atcomparatively little expense into existing process sequences and issuitable for mass production, or in other words that enables a highyield of finished semiconductor circuit devices or semiconductor memorydevices with ferroelectric storage capacitors, with the least possiblenumber of premature failures.

With the foregoing and other objects in view there is provided, inaccordance with the invention, a method for producing a capacitor havinga dielectric, a first capacitor electrode and a second capacitorelectrode in a semiconductor circuit device formed on a semiconductorsubstrate, which comprises forming a trench in a layer applied to thesubstrate of the semiconductor circuit device; depositing anelectrically conductive layer for the second capacitor electrode in adeposition being inside the trench and at least regionally conformalwith side walls of the trench; conformally depositing an auxiliary layeracting as a space-holder for the dielectric in a deposition being insidethe trench and on the electrically conductive layer for the secondcapacitor electrode; conformally depositing an electrically conductivelayer for the first capacitor electrode in a deposition being inside thetrench and on the auxiliary layer; at least partial removing theauxiliary layer and exposing a hollow layer in at least a partial regionbetween the two electrically conductive layers for the first and secondcapacitor electrodes; and depositing the dielectric into the exposedhollow layer between the two electrically conductive layers for thefirst and second capacitor electrodes.

In accordance with another mode of the invention, the step of depositionof the dielectric layer is performed through the use of spin-on coating.

In accordance with a further mode of the invention, the dielectriclayers are applied with a layer thickness in the manometer range, whichbecause of their viscous, paintlike consistency can preferably beapplied by spin-on coating.

The dielectric, having a material which is preferably in the form of asubstrate introduced by spin-on coating in a solvent, is deposited intothe exposed hollow layer between the two electrically conductive layersfor the first and second capacitor electrodes.

In accordance with an added mode of the invention, the dielectric is aferroelectric gel that is applied by spin-on coating. Moreover, thedielectric may also be some other, not necessarily ferroelectricsubstance that can be applied by the spin-on coating process, namely asubstance for the dielectric having a higher dielectric constant thanthe previously known substances.

With the objects of the invention view there is also provided asemiconductor memory device, comprising a semiconductor substrate havinga surface defining a plane extending substantially parallel to thesurface; a multiplicity of memory cells disposed on the semiconductorsubstrate; each of the memory cells including a selection transistorbeing disposed in the plane and having a gate terminal, a firstelectrode terminal and a second electrode terminal, the second electrodeterminal having a contact metallizing layer with a given layerthickness; each of the memory cells including a storage capacitor beingassociated with and triggerable by the selection transistor, the storagecapacitor having a ferroelectric dielectric, a first capacitor electrodeand a second capacitor electrode, the storage capacitor having aconfiguration projecting upward from the plane, the storage capacitorbeing disposed in a trench formed inside the contact metallizing layer,and the trench having a depth being equivalent to the given layerthickness; a word line to which the gate terminal of each of theselection transistors is connected; a bit line to which the firstelectrode terminal of each of the selection transistors is connected;and a common conductor layer of electrically conductive material towhich the first capacitor electrode of each of the storage capacitors isconnected.

This embodiment of the storage capacitor with the ferroelectricdielectric in an upward-projecting configuration makes it possible, withthe smallest possible surface area of the FRAM cell, to neverthelessachieve an adequate capacitance of the storage capacitor. The embodimentaccording to the invention with a configuration of the ferroelectricstorage capacitor that projects upward from the plane of the substratesurface permits the use of the ferroelectric, which is considered to becritical in view of the desired large scale of integration, aftercomplete production of the components of the memory cell that are lesscritical in this respect, that is selection transistors with completemetallizing including associated electrodes. This is preferably carriedout in such a way that. The ferroelectric gel to be applied through theuse of spin technology is applied inside a thin hollow layer formedbetween the two capacitor electrodes. The hollow layer likewise has aconfiguration that projects upward from the plane of the substratesurface.

In accordance with another feature of the invention, the storagecapacitor having the ferroelectric dielectric projecting upward from theplane of the substrate surface is constructed substantiallycylinder-symmetrically, with a center axis of the cylinder extendingapproximately perpendicular to the plane of the substrate surface.

In accordance with a further feature of the invention, the secondcapacitor electrode of the storage capacitor is constructed inside thetrench as a metal spacer deposited conformally onto vertical side wallsof the trench.

In accordance with an added feature of the invention, the firstcapacitor electrode of the storage capacitor has an electrode segmentformed inside the trench and extending coaxially with the lengthwiseextension of the trench and opposite the second capacitor electrode, andthe ferroelectric dielectric is disposed at least between the electrodesegment of the first capacitor electrode and the second capacitorelectrode.

In accordance with an additional feature of the invention, the firstcapacitor electrode of the storage capacitor is constructed in cup-likefashion inside the second capacitor electrode.

With the objects of the invention view there is additionally provided amethod for producing a semiconductor memory device, which comprisesplacing a multiplicity of memory cells on a semiconductor substratehaving a surface; providing each of the memory cells with a selectiontransistor being disposed in a plane extending substantially parallel tothe surface of the substrate and having a gate terminal, a firstelectrode terminal and a second electrode terminal; providing each ofthe memory cells with a storage capacitor being associated with andtriggerable by the selection transistor and having a ferroelectricdielectric, a first capacitor electrode and a second capacitorelectrode; connecting the gate terminal of each selection transistor toa word line of the semiconductor memory device; connecting the firstelectrode terminal of the selection transistor to a bit line; connectingeach first capacitor electrode of the storage capacitor to a commonconductor layer of electrically conductive material; producing thestorage capacitor after production of the selection transistor andmetallizing layers associated with the storage capacitor for connectionof the word and bit lines, in a configuration projecting upward from theplane; placing the storage capacitor in a trench formed inside a contactmetallizing layer for the second electrode terminal of the selectiontransistor; and setting a depth of the trench to be equivalent to alayer thickness of the contact metallizing layer.

In this case the concept of the method of the invention is basedinitially on the recognition of disclosing a semiconductor memory deviceor a process sequence for producing the semiconductor memory device, inwhich the ferroelectric materials can be successfully tied into theprocess sequence for producing the semiconductor memory device,specifically by providing that not until after the production of thecompletely constructed selection transistors, together with completemetallizing and including all of the electrodes associated with theselection transistor, is the dielectric material applied and subjectedto a heat treatment to perform the necessary crystallization.

The method of the invention makes it possible to produce a FRAM memorydevice having a surface area requirement which is as slight as that fora RTAM cell, specifically through the use of a sequence of process stepsthat can be integrated into existing process sequences. In particular,the layer thickness of the ferroelectric dielectric can be adjustedexactly, preferably in the nm range.

In accordance with another mode of the invention, the method forproducing a semiconductor memory device with a storage capacitor havinga ferroelectric dielectric is performed by the following steps, afterproduction of the selection transistor: full-surface application of aninsulation cover layer; formation of a contact metallizing layer for thesecond electrode terminal of the selection transistor; etching of atrench, extending as far as the insulating cover layer, inside thecontact metallizing layer; deposition, in a manner conformal to the sidewalls of the trench, of an electrically conductive layer for the secondcapacitor electrode inside the trench; conformal deposition of anauxiliary layer, acting as a space-holder for the ferroelectricdielectric, inside the trench and onto the electrically conductive layerfor the second capacitor electrode; conformal deposition of anelectrically conductive layer for the first capacitor electrode insidethe trench and onto the auxiliary layer; at least partial removal of theauxiliary layer and resultant exposure of a hollow layer in at least apartial region between the two electrically conductive layers for thefirst and second capacitor electrodes; and deposition of theferroelectric dielectric into the exposed hollow layer between the twoelectrically conductive layers for the first and second capacitorelectrodes.

In accordance with a further mode of the invention, the step ofdepositing the dielectric layer having the ferroelectric dielectric iscarried out through the use of spin-on coating.

In accordance with an added mode of the invention, the method includesback-etching of the electrically conductive layer deposited conformallywith the inner contour of the trench for the second capacitor electrode,at least far enough to ensure that the portion of the electricallyconductive layer, deposited in planar fashion outside the trench, forthe second capacitor electrode, is removed. In this way, the danger ofan electrical short circuit of the two capacitor electrodes is reduced.

In an especially preferred feature of the semiconductor memory device orof the method of the invention, the ferroelectric dielectric is aferroelectric gel, which in particular has a lead zirconium titanate(PZT) and/or a strontium tantalate compound.

The material including the layer for the first and/or second capacitorelectrode also preferably has titanium and/or platinum, wherein thelayer for the first and/or the second capacitor electrode may also beconstructed as a multiple layer, preferably with a layer sequence oftitanium/titanium nitride/platinum or titanium/titaniumnitride/tungsten.

Other features which are considered as characteristic for the inventionare set forth in the appended claims.

Although the invention is illustrated and described herein as embodiedin a method for producing a capacitor and a semiconductor memory device,it is nevertheless not intended to be limited to the details shown,since various modifications and structural changes may be made thereinwithout departing from the spirit of the invention and within the scopeand range of equivalents of the claims.

The construction and method of operation of the invention, however,together with additional objects and advantages thereof will be bestunderstood from the following description of specific embodiments whenread in connection with the accompanying drawings.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a basic schematic circuit diagram of a semiconductor deviceaccording to the invention having a FRAM cell; and

FIGS. 2-4 are fragmentary, diagrammatic, sectional views showingsuccessive method steps in the production of the semiconductor memorydevice of the invention.

DESCRIPTION OF THE PREFERRED EMBODIMENTS

Referring now to the figures of the drawings in detail and first,particularly, to FIG. 1 thereof, there is seen a substitute circuitdiagram of a semiconductor memory device of the invention having a ERMcell 1 with a selection transistor 3, preferably of the MOS type, whichis formed on a semiconductor substrate 2 (shown in FIG. 2) and which hasa first electrode terminal 5 (source) connected to a bit line 4 made oftungsten or polycide, a second electrode terminal 6 (drain) and a gateterminal 8 connected to a word line 7 made of n⁺ polysilicon orpolycide. The FRAM cell 1 also has a storage capacitor 9 with a firstcapacitor electrode 11 connected to a common conductor layer 10 (fieldplate), a second capacitor electrode 12 connected to the secondelectrode terminal 6 of the selection transistor 3 and a ferroelectricdielectric 13 inserted between the first and second capacitorelectrodes.

The point of departure of the exemplary embodiment of the method of theinvention for producing the semiconductor memory device shown in FIGS.2-4 is a configuration that is shown in FIG. 2 through the use of methodsteps which are known from the DRAM process up to and including theproduction of the bit line 4. In this configuration, a planarizedinsulated cover layer 15, for instance a BPSG flow glass, is depositedover the entire surface. A self-adjusted (overlapping) contactmetallizing layer 16 for connection of an n⁺-doped drain region 17 (ofthe second electrode terminal 6) of the selection transistor 3 is alsoformed. The contact metallizing layer 16 is deposited conformally,preferably as an n⁺ polysilicon layer with a thickness of approximately0.7 μm.

Subsequently, through the use of an anisotropic etching operation, atrench 18 that is constructed to project upward from a plane 21 of thesubstrate surface, is formed in the contact metallizing layer 16. It isdisposed directly above the region of the selection transistor 3 andextends as far as the BPSG layer 15.

Subsequently, as is shown in FIG. 3, an electrically conductive layer19, that is a metal space-holder (“spacer”) is produced at vertical sidewalls of the trench 18 through the use of conformal deposition andensuing anisotropic back-etching of the electrically conductive layer19. The space-holder (spacer) preferably has layers in the order ofTi/TiN/Pt or Ti/TiN/W.

As is shown in FIG. 3, an auxiliary layer 20 of SiO₂ is depositedconformally inside the trench 18 onto the electrically conductive layer19 on the thus-created configuration. The layer 20 acts as aspace-holder for the ferroelectric dielectric and the thickness of theSiO₂ auxiliary layer 20 is equivalent to the later ferroelectric layer.In order to produce the common capacitor plate 10, an electricallyconductive layer 23, preferably including a high-temperature-stablemetal such as platinum or tungsten, is deposited conformally onto theSiO2 auxiliary layer 20. A remaining hollow space in the trench 18 isfilled with a suitable filler material 22. The filler material 22, forinstance including polysilicon, is deposited conformally and ispreferably anisotropically back-etched. In this way, the configurationshown in FIG. 3 is created.

In the next step, the electrically conductive layer 23 includingplatinum or tungsten is back-etched at least far enough to ensure that aportion 24 of the electrically conductive layer 23 located at horizontalregions is removed.

After a heat treatment is performed, with attendant curing of all of theprior process steps, the material of the auxiliary layer 20 acting as aspace-holder for the ferroelectric dielectric is etched free, preferablywet chemically, for instance with dilute hydrofluoric acid, specificallyat least far enough to ensure that a hollow layer 25 orientedsubstantially nearly vertically from the plane 21 of the substratesurface is formed between the two layers 19 and 23 for the capacitorelectrodes 11 and 12. In this hollow layer, a thin film of aferroelectric gel is then applied, preferably through the use ofspin-coating (spin-on technology). Voids between the two capacitorplates 19 and 23 are filled with the ferroelectric gel in the process.The ferroelectric dielectric is subjected to a heat treatment step forthe sake of crystal formation in it. A bottom 26 left standing in thewet chemical etching of the material including the auxiliary layer 20serves to mechanically brace the first capacitor electrode 11 locatedcoaxially inside the trench 18.

Next, as is shown in FIG. 4, a passivation layer 27, preferably of SiO₂,is deposited over the entire surface.

This can be followed by further process steps in a manner that is knownper se, for instance for metallizing.

We claim:
 1. A method for producing a capacitor having a dielectric, afirst capacitor electrode and a second capacitor electrode in asemiconductor circuit device formed on a semiconductor substrate, whichcomprises: forming a trench in a layer applied to the substrate of thesemiconductor circuit device; depositing an electrically conductivelayer for the second capacitor electrode in a deposition being insidethe trench and at least regionally conformal with side walls of thetrench; conformally depositing an auxiliary layer acting as aspace-holder for the dielectric in a deposition being inside the trenchand on the electrically conductive layer for the second capacitorelectrode; conformally depositing an electrically conductive layer forthe first capacitor electrode in a deposition being inside the trenchand on the auxiliary layer; at least partial removing the auxiliarylayer and exposing a hollow layer in at least a partial region betweenthe two electrically conductive layers for the first and secondcapacitor electrodes; and depositing the dielectric into the exposedhollow layer between the two electrically conductive layers for thefirst and second capacitor electrodes.
 2. The method for producing acapacitor according to claim 1, which comprises performing the step ofdeposition of the dielectric layer by spin-on coating.
 3. The method forproducing a capacitor according to claim 1, which comprises applying orspin-coating the dielectric in the form of a substance being introducedin a solvent and having a viscous, paint-like consistency.
 4. The methodfor producing a capacitor according to claim 1, which comprisesdepositing a ferroelectric gel as the dielectric.
 5. The method forproducing a capacitor according to claim 1, which comprises depositing aferroelectric gel having a compound selected from the group consistingof lead-zirconium-titanate and a strontium-tantalate as the dielectric.6. The method for producing a capacitor according to claim 1, whichcomprises depositing a material containing SiO₂ as the auxiliary layeracting as a space-holder for the dielectric.
 7. The method for producinga capacitor according to claim 1, which comprises forming the trenchwith a depth being equivalent to a thickness of the layer.